Ogbomo, OO, Amalu, EH, Ekere, NN and Olagbegi, PO (2018) Effect of operating temperature on degradation of solder joints in crystalline silicon photovoltaic modules for improved reliability in hot climates. Solar Energy, 170. pp. 682-693. ISSN 0038-092X

Preview

Text Effect of operating temperature on degradation of solder joints in crystalline silicon photovoltaic modules.pdf - Accepted Version Available under License Creative Commons Attribution Non-commercial No Derivatives. Download (909kB) | Preview

Abstract

Accelerated degradation of solder joint interconnections in crystalline silicon photovoltaic (c-Si PV) modules drives the high failure rate of the system operating in elevated temperatures. The phenomenon challenges the thermo-mechanical reliability of the system for hot climatic operations. This study investigates the degradation of solder interconnections in c-Si PV modules for cell temperature rise from 25 °C STC in steps of 1 °C to 120 °C. The degradation is measured using accumulated creep strain energy density (Wacc). Generated Wacc magnitudes are utilised to predict the fatigue life of the module for ambient temperatures ranging from European to hot climates. The ANSYS mechanical package coupled with the IEC 61,215 standard accelerated thermal cycle (ATC) profile is employed in the simulation. The Garofalo creep model is used to model the degradation response of solder while other module component materials are simulated with appropriate material models. Solder degradation is found to increase with every 1 °C cell temperature rise from the STC. Three distinct degradation rates in Pa/°C are observed. Region 1, 25 to 42 °C, is characterised by degradation rate increasing quadratically from 1.53 to 10.03 Pa/°C. The degradation rate in region 2, 43 to 63 °C, is critical with highest constant magnitude of 12.06 Pa/°C. Region 3, 64 to 120 °C, demonstrates lowest degradation rate of logarithmic nature with magnitude 5.47 at the beginning of the region and 2.25 Pa/°C at the end of the region. The module fatigue life, L (in years) is found to decay according to the power function L=721.48T-1.343. The model predicts module life in London and hot climate to be 18.5 and 9 years, respectively. The findings inform on the degradation of c-Si PV module solder interconnections in different operating ambient temperatures and advise on its operational reliability for improved thermo-mechanical design for hot climatic operations.

Item Type:	Article
Uncontrolled Keywords:	09 Engineering, 12 Built Environment and Design
Subjects:	T Technology > TA Engineering (General). Civil engineering (General)
Divisions:	Engineering
Publisher:	Elsevier
Date Deposited:	02 Nov 2021 11:42
Last Modified:	02 Nov 2021 11:45
DOI or ID number:	10.1016/j.solener.2018.06.007
URI:	https://researchonline.ljmu.ac.uk/id/eprint/15727

View Item